Easily Applicable Superhydrophobic Composite Coating with Improved Corrosion Resistance and Delayed Icing Properties

Mitigating the adverse effects of corrosion failure and low-temperature icing on aluminum (Al) alloy materials poses significant research challenges. The facile fabrication of bioinspired superhydrophobic materials offers a promising solution to the issues of corrosion and icing. In this study, we utilized laboratory-collected candle soot (CS), hydrophobic fumed SiO₂, and epoxy resin (EP) to create a HF-SiO₂@CS@EP superhydrophobic coating on Al alloy surfaces using a spray-coating technique. Various characterization techniques, including contact angle meter, high-speed camera, FE-SEM, EDS, FTIR, and XPS, were employed to investigate surface wettability, morphologies, and chemical compositions. Moreover, a 3.5 wt.% NaCl solution was used as a corrosive medium to evaluate the corrosion resistance of the uncoated and coated samples. The results show that the capacitive arc radius, charge transfer resistance, and low-frequency modulus of the coated Al alloy significantly increased, while the corrosion potential (<i>E</i>_corr) shifted positively and the corrosion current (<i>I</i>_corr) decreased by two orders of magnitude, indicating improved corrosion resistance. Additionally, an investigation of ice formation on the coated Al alloy at -10 °C revealed that the freezing time was 4.75 times longer and the ice adhesion strength was one-fifth of the uncoated Al alloy substrate, demonstrating superior delayed icing and reduced ice adhesion strength performance.