Analysis of the gas pipeline defects formation mechanism as a result of arc discharge impact on the pipe wall

The article presents an analysis of the formation possibility through defects in a gas pipeline as a result of short-term exposure to an arc discharge. The results of metallography, electron microscopy, elemental analysis, as well as the modeling results, confirming the formation possibility through defects in a 7 mm thick gas pipeline wall during an exposure to an arc discharge of less than 2 seconds are presented.