Investigation of Tribological Behavior of PTFE Composites Reinforced with Bronze Particles by Taguchi Method

Reinforced PTFE materials can be designed to show high mechanical stability against harder materials under sliding wear conditions. Especially bearing metal-reinforced PTFE is of high practical interest. In this class of materials, bronze-filled PTFE was reported to obtain high wear resistance, a low coefficient of friction (COF), and excellent self-lubrication properties in sliding conditions. In the statistical approach of this work, PTFE composites reinforced with 25 vol%, 40 vol%, and 60 vol% bronze particles were evaluated against pure PTFE regarding wear behavior under varied wear test parameters, i.e., material, normal load, and sliding speed. Wear tests were planned to use a standard orthogonal array based on the Taguchi design method. An analysis of variance test was utilized to quantify the effects of test parameters on the wear behavior of the bronze/PTFE composites and pure PTFE. According to the variance analysis, the material type has the largest influence on the COF and the specific wear rate (SWR) under test conditions of this work. Both COF and SWR were found to be influenced by the material type (29.83% and 96.16%), the normal load (33.34% and 0.95%), and sliding speed (9.14% and 1.28%). The lowest SWR and COF values were achieved at the optimum wear test conditions where the wear test parameters were 1 m/s sliding speed (A4B2C2) at PTFE + 60 vol.% bronze reinforced composite 50 N application load and 0.32 m/s sliding speed (A4B3C1) at PTFE + 60 vol.% bronze reinforced composite 100 N application load, respectively.