Chitosan enriched with ZnO nanoparticles fabricated using Synadenium glaucescens (Pax) aqueous leaf extract maintains postharvest quality of banana

• Zinc oxide nanoparticles were successfully synthesized using Synadenium glaucescens (Pax) aqueous leaf extract and incorporated into chitosan film as an antimicrobial agent. • The mixture of chitosan and fabricated zinc oxide nanoparticles produced a film with synergistic antimicrobial effects. • The film containing the chitosan and fabricated zinc oxide nanoparticles mixture maintained postharvest qualities of banana such as titratable acidity, total soluble solids, weight loss and ripening index. • The film of chitosan and fabricated zinc oxide nanoparticles may serve as an effective preservative of post-harvest qualities of banana and related fruits. Applications of edible coatings containing metallic nanoparticles for the preservation of post-harvest fruit quality have emerged as one of the most preferable strategies because of their enhanced antimicrobial properties. In the current study, zinc oxide nanoparticles were synthesized using Synadenium glaucescens leaf extract and added to chitosan for the post-harvest quality preservation of banana. The synthesized zinc oxide nanoparticles (ZnOSydlNPs) were characterized using scanning electron microscopy (SEM), transmission electron microscopy (TEM), elemental dispersive x-ray (EDX) and X-ray diffraction (XRD) techniques. The nanoparticles were found to form large particles due to aggregations of small particles of an average size of 11 ± 4 nm. The coating solution containing a mixture of chitosan and zinc oxide nanoparticles exhibited higher antimicrobial effects against Escherichia coli, Staphylococcus aureus, Puccinia asparagi and Candida albicans compared to chitosan. The inhibition diameters of chitosan and chitosan-ZnOSydlNPs against E. coli were 6 and 15 mm, respectively. Similarly, the average inhibition diameters of chitosan, chitosan-ZnOSydlNPs (0.1%) and chitosan-ZnOSydlNPs (0.3%) against Staphylococcus aureus, Puccinia asparagi and Candida albicans were 10 ± 2, 15 ± 0.5 and 16 ± 3 mm, respectively. The banana coated with chitosan-ZnOSydlNPs solutions exhibited higher titratable acid (maleic) than control and chitosan-coated samples. Additionally, banana coated with chitosan-ZnOSydlNPs films showed lower total soluble solids, weight loss and ripening index compared to chitosan-coated and control samples. The findings from the current study indicated that ZnOSydlNPs incorporated in polymeric materials (chitosan) could serve as a potential preservative of post-harvest qualities for banana and related fruits.