Tailoring sub-5 nm Fe-doped CeO2 nanocrystals within confined spaces to boost photocatalytic hydrogen evolution under visible light

The reverse micelles route allows for obtaining sub-5 nm Fe-doped CeO 2 catalysts for hydrogen photoproduction under visible light with high stability and remarkable photoactivity compared to the conventional precipitation method. This work aimed to study the efficiency of the reverse micelle (RM) preparation route in the syntheses of sub-5 nm Fe-doped CeO 2 nanocrystals for boosting the visible-light-driven photocatalytic hydrogen production from methanol aqueous solutions. The effectiveness of confining precipitation reactions within micellar cages was evaluated through extensive physicochemical characterization. In particular, the nominal composition (0–5 mol% Fe) was preserved as ascertained by ICP-MS analysis, and the absence of separate iron-containing crystalline phases was supported by X-ray diffraction. The effective aliovalent doping and modulation of the optical properties were investigated using UV-Vis, Raman, and photoluminescence spectroscopies. 2.5 mol% iron was found to be an optimal content to achieve a significant decrease in the band gap, enhance the concentration of oxygen vacancy defects, and increase the charge carrier lifetime. The photocatalytic activity of Fe-doped CeO 2 prepared at different Fe contents with RM preparation was studied and compared with undoped CeO 2 . The optimal iron load was identified to be 2.5 mol%, achieving the highest hydrogen production (7566 μmol L −1 after 240 min under visible light). Moreover, for comparison, the conventional precipitation (P) method was adopted to prepare iron containing CeO 2 at the optimal content (2.5 mol% Fe). The Fe-doped CeO 2 catalyst prepared by RM showed a significantly higher hydrogen production than that obtained with the sample prepared by the P method. The optimal Fe-doped CeO 2 , prepared by the RM method, was stable for six reuse cycles. Moreover, the role of water in the mechanism of photocatalytic hydrogen evolution under visible light was studied through the test in the presence of D 2 O. The obtained results evidenced that hydrogen was produced from the reduction of H + by the electrons promoted in the conduction band, while methanol was preferentially oxidized by the photogenerated positive holes.