Power ultrasound-assisted enhancement of granulated blast furnace slag reactivity in cement paste

This paper introduces a first-time investigation into the impact of power ultrasound (PUS)-assisted preparation on the physicochemical and mechanical properties of cement-granulated blast furnace slag (GBFS) composite pastes. Pastes containing deposited GFBS with varying particle size fractions, partially replacing Portland cement, were prepared using PUS (ultrasonic horn tip, 20 kHz, 700 W) in pulse mode in a vertical jacketed glass sonoreactor with closed-circuit cooling. Cement paste incorporating 20 wt.% GBFS as mass substitution with varying particle size fractions was characterized by several physicochemical techniques at different curing ages. Exploring the cement and GBFS interaction induced by PUS, the compressive and flexural strength, the elastic modulus and indentation hardness, the heat of hardening, the mineral composition of hydration products, and the specific surface area BET were evaluated for a curing time of up to 28 days. The grain size distribution of GFBS and the reaction mixture's pH were measured. Both mechanical properties, heat of hydration and nanoporosity exhibited strong sensitivity to PUS treatment. Sonofragmentation of GBFS particles (especially the 125–250 μm fraction) increased with increasing sonication time, resulting in a relative increase of fraction <63 μm and a decrease of fraction >125 μm by 275 % and 60 %, respectively. Using the obtained SEM-EDS data, a simplified mechanism is proposed to explain the effects induced by PUS treatment.