Mechanical Properties and Energy Absorption Characteristics of Additively Manufactured Lattice Structures of a High‐Temperature Titanium Matrix Composite

Lightweight lattice structure is of great significance in the fields of aerospace thermal protection and energy absorption. In this study, compressive properties and energy‐absorbing characteristics of additively manufactured body‐centered cubic (BCC) lattice structures of a high‐temperature titanium matrix composite (TMC) are investigated systematically. It is found that compressive strength increases monotonically as either lattice strut diameter or temperature increases. With lattice strut diameter increasing from 1.0 to 1.5 and 2.0 mm, strength increases from 78 to 94 and 108 MPa at room temperature (RT) and from 71 to 104 and 123 MPa at 650 °C. Unexpectedly, specific energy absorption (SEA) capability increases as strut diameter decreases, although also increases as temperature increases. BCC lattice structure with a strut diameter of 1.0 mm presents the highest SEA being up to 13.7 MJ m −3 at RT and 142 MJ m −3 at 650 °C. And sphericizing the lattice nodes is found incapable of enhancing strength and SEA. Besides, numerical simulation is used to demonstrate the compressive stress and strain fields, in order to explain the fracture modes and SEA capability of individual BCC lattice structures. This study provides deep insights into the mechanical properties and energy absorption behavior of additively manufactured lattice structures of TMCs.