Powder coarsening mechanisms of Ti-6Al-4 V with multiple build cycles in laser powder bed fusion

Abstract Laser powder bed fusion (LPBF) is an additive manufacturing process which can produce complex 3D parts from digital models. The performance of parts fabricated by LPBF is largely dependent on the characteristics of the powder feedstock, in particular, the particle size distribution. The coarsening of powder particles may limit the potential for reusing powder in further builds, as consistency in powder quality is crucial for ensuring consistent parts performance when using reused powder, especially in aerospace applications. However, there is a lack of systematic understanding regarding the causes and nature of powder coarsening in LPBF. In this work, the characteristics of powder samples from different locations in the build chamber during LPBF were studied to understand the particle size evolution and determine the origin of coarsening, which has not been previously reported. Meanwhile, powder coarsening was found to have a detrimental effect on the relative density and surface quality of as-built parts, highlighting the importance of exploring the mechanisms of powder coarsening and finding ways to control it in LPBF. The relationship between powder in key locations in the build chamber and its effect on powder coarsening has been established. Layer thickness is identified as a critical factor in causing powder coarsening due to the fine powder size characteristic in the powder bed. Spatter, in its various forms, plays a direct or indirect role in powder coarsening. Sintered powders resulting from spatter and the laser scanning borders of as-built parts were observed to contribute to the powder coarsening. Therefore, three main mechanisms (layer thickness, spatter, sintered powder) associated with the powder coarsening are therefore proposed. This work provides insight and potential solutions to control powder coarsening and maintain consistent parts performance.