Comparison of Levitation Properties between Bulk High-Temperature Superconductor Blocks and High-Temperature Superconductor Tape Stacks Prepared from Commercial Coated Conductors

Bulk high-temperature superconductors (HTSs) such as <i>RE</i>Ba₂Cu₃O_7-x (<i>RE</i>BCO, <i>RE</i> = Y, Gd) are commonly used in rotationally symmetric superconducting magnetic bearings. However, such bulks have several disadvantages such as brittleness, limited availability and high costs due to the time-consuming and energy-intensive fabrication process. Alternatively, tape stacks of HTS-coated conductors might be used for these devices promising an improved bearing efficiency due to a simplification of manufacturing processes for the required shapes, higher mechanical strength, improved thermal performance, higher availability and therefore potentially reduced costs. Hence, tape stacks with a base area of (12 × 12) mm² and a height of up to 12 mm were prepared and compared to commercial bulks of the same size. The trapped field measurements at 77 K showed slightly higher values for the tape stacks if compared to bulks with the same size. Afterwards, the maximum levitation forces in zero field (ZFC) and field cooling (FC) modes were measured while approaching a permanent magnet, which allows the stiffness in the vertical and lateral directions to be determined. Similar levitation forces were measured in the vertical direction for bulk samples and tape stacks in ZFC and FC modes, whereas the lateral forces were almost zero for stacks with the <i>RE</i>BCO films parallel to the magnet. A 90° rotation of the tape stacks with respect to the magnet results in the opposite behavior, i.e., a high lateral but negligible vertical stiffness. This anisotropy originates from the arrangement of decoupled superconducting layers in the tape stacks. Therefore, a combination of stacks with vertical and lateral alignment is required for stable levitation in a bearing.