Investigation into the Fuel Characteristics of Biodiesel Synthesized through the Transesterification of Palm Oil Using a TiO2/CH3ONa Nanocatalyst

Biodiesel is a renewable and sustainable alternative fuel to petrol-derived diesel. Decreasing the operating costs by improving the catalyst’s characteristics is an effective way to increase the competitiveness of biodiesel in the fuel market. An aqueous solution of sodium methoxide (CH3ONa), which is a traditional alkaline catalyst, was immersed in nanometer-sized particles of titanium dioxide (TiO2) powder to prepare the strong alkaline catalyst TiO2/CH3ONa. The immersion method was used to enhance the transesterification reaction. The mixture of TiO2 and CH3ONa was calcined in a high-temperature furnace in a range between 150 and 450 °C continuously for 4 h. The heterogeneous alkaline catalyst TiO2/CH3ONa was then used to catalyze the strong alkaline transesterification reaction of palm oil with methanol. The highest content of fatty acid methyl esters (FAMEs), which amounted to 95.9%, was produced when the molar ratio of methanol to palm oil was equal to 6, and 3 wt.% TiO2/CH3ONa was used, based on the weight of the palm oil. The FAMEs produced from the above conditions were also found to have the lowest kinematic viscosity of 4.17 mm2/s, an acid value of 0.32 mg KOH/g oil, and a water content of 0.031 wt.%, as well as the highest heating value of 40.02 MJ/kg and cetane index of 50.05. The lower catalyst amount of 1 wt.%, in contrast, resulted in the lowest cetane index of 49.31. The highest distillation temperature of 355 °C was found when 3 wt.% of the catalyst was added to the reactant mixture with a methanol/palm oil molar ratio of 6. The prepared catalyst is considered effective for improving the fuel characteristics of biodiesel.