In Situ Metallic Bi-Modified (110)BiOBr Nanosheets with Surface Plasmon Resonance Effect for Enhancing Photocatalytic Performance Despite of Larger Optical Band Gap

BiOBr with different preferred growth orientation facets would show a different photocatalytic performance. When decorated in situ with metallic Bi nanoparticles, Bi/BiOBr would commonly display an enhanced photocatalytic performance. In this paper, the BiOBr nanoplates with preferred growth orientation (102) facet and (110) facet were first synthesized using a hydrothermal method. Then, some metallic Bi nanoparticles were modified in situ onto the (110)BiOBr nanoplates, which was expected to show a much more enhanced photocatalytic performance. All samples were characterized using XRD, FE-SEM, TEM, N2 adsorption–desorption, UV–vis and XPS. FE-SEM and TEM images showed that the grain size of the metallic Bi particles was about 5 nm to 10 nm. UV–vis spectra showed that, after some metallic Bi nanoparticles were modified on (110)BiOBr nanoplates, the light absorbance in the visible light region at 400–700 nm became stronger and their optical band gap became larger. N2 adsorption–desorption tests showed that the Bi(x)/(110)BiOBr nanosheets possessed larger specific surface areas than that of the (102)BiOBr and (110)BiOBr nanoplates. The XPS results showed that Bi(x)/(110)BiOBr contained more oxygen vacancies and a more negative value of the conduction band minimum. The photocatalytic performance of (102)BiOBr, (110)BiOBr and Bi(x)/(110)BiOBr were tested in the photocatalytic degradation of rhodamine B under visible light irradiation for 2 h; their photocatalytic efficiency was 45%, 75% and 80%, respectively. In comparison to (102)BiOBr, (110)BiOBr exhibited much higher photocatalytic activity, while for Bi(x)/(110)BiOBr, despite the surface Plasmon resonance effect, a larger specific surface area and more oxygen vacancies, the enhancement of the efficiency was limited, which might have resulted from the larger optical band gap.