Stretchable Composite Films Are Prepared by Using Cellulose Pulp with Differential Substitution of Carboxymethyl Cellulose and Thymol with an Infrared Heating Process for Packaging Application

Herein, cellulose pulp (CP), carboxymethyl cellulose (CMC), and thymol-based eco-friendly, transparent, and flexible composite films are prepared. These materials dissolved well in an environment-friendly process in <i>N</i>-methyl morpholine <i>N</i>-oxide (NMMO) ionic liquids using infrared heating. Fourier-transform infrared spectroscopy (FT-IR), X-ray diffraction (XRD), and scanning electron microscopy (SEM) analyses are used to study the structure, microstructure, and morphology of the composite films. The thermal properties of the CP/CMC/thymol composites are thoroughly studied by thermogravimetric analysis (TGA) and differential scanning calorimetry (DSC). The thermal stability of the composites (<i>T</i> _5%-57.8-91.2 °C and <i>T</i> _10%-216.6-284.1 °C) significantly improves following the CMC addition. In each case, all the composite film exhibits unique <i>T</i> _g (140.5-143.1 °C) values, as confirmed by DSC. The tensile strength of the cellulose pulp is 66.5 MPa, increasing to 78.4 MPa for the CP/CMC-1:0.5 composites and steadily increasing to 93.8 MPa with increasing CMC content. Similarly, CMC increases the EB of cellulose pulp from 9.3 to 7.4%. The water vapor permeability and swelling ratio values of the CP/CMC/thymol composites are in the range of 1.9-2.11 × 10^-9 g/(m²·Pa·s) and 52.5-50.8° respectively. The CP, CMC, and thymol-based composite do not exhibit cytotoxicity to the aneuploid immortal keratinocyte cell line and demonstrate excellent antioxidant properties, for promising packaging and biomedical applications.