Research on the Compressive Strength of Saltwater Mixing and Curing Cement Mortar Incorporating Blast Furnace Slag

In this study, the blast furnace slag (BFS) was used to replace 30% cement (weight replacement), freshwater, and saltwater (half, same, and twice the concentration of seawater) used to produce the cement mortar. Then, these four types of mixing water were used to cure the mortar till the test ages (7 days and 28 days). The test results show that, at 7 days, the compressive strength of saltwater (half concentration) mixing and curing mortar incorporating BFS is the highest (78 MPa). The freshwater mixing and curing control mortar has the lowest compressive strength (36.2 MPa). At 28 days, the compressive strength of saltwater (twice concentration) mixing and saltwater (half concentration) curing mortar incorporating BFS is the highest (90.2MPa). The strength of the control mortar is 53.0MPa under the same curing water, which is still relatively low. It can be seen from this that the mixing and curing of saltwater are beneficial to improving the compressive strength of cement mortar. The freshwater mixing and saltwater (twice concentration) curing cement mortar incorporating 30% BFS can have a higher strength at 28 days.