Effect of Electron Irradiation on the Optical Properties of Zinc Oxide Powder Modified by Magnesium Oxide Nanoparticles

The effect of modifying ZnO powders with MgO nanoparticles (with a concentration of 0.1–10 wt. %) on their diffuse reflectance spectra in the region of 0.2–2.5 μm before and after irradiation with 30 keV electrons was studied. Modification of ZnO powder was carried out by MgO nanopowder with concentrations from 0.1 to 10 wt. % using a solid-state method at 650°C heating temperature. X-ray diffraction analysis showed that this method of modification there is no formation of additional phases. It has been established that zinc oxide structure symmetry belongs to the P63mc space group, magnesium oxide – to the Fm–3m space group. The spectral reflectance of such powders in the visible region is over 90%. Under irradiating by 30 keV electrons of initial and modified ZnO powders, as well as MgO nanopowder, a decrease in their reflectance recorded in the entire studied region of the spectrum. It has been established that modification with MgO nanoparticles at a concentration of 3 wt. % leads to an increase in radiation resistance by a factor of 1.32 compared to unmodified samples. This effect is determined by the sink of radiation defects on the large specific surface area of nanoparticles.