Analysis of the Surface Morphology and Chemical Composition of Zr-Nb3Sn Alloys with Different Zr Concentrations

In the field of superconducting science, Nb has been the material of choice for Radio Frequency (RF) Cavities for years. However, in recent years Nb3Sn has shown to be a promising alternative to Nb. Its combination of a significantly high superconducting transition temperature and a much higher value of upper critical magnetic field (Hc2), has been the reason the alloy has been so widely studied. This project aims to develop materials to further improve the high magnetic field performance of Nb3Sn by improving its upper critical magnetic field and critical current density (Jc). One way to improve the Jc and the Hc2 is to create more grain boundaries in the Nb3Sn alloy allowing them to trap more magnetic flux lines in the materials. To do this the grains must be made smaller which will naturally cause the formation of more grain boundaries. A common way to create smaller grains is by doping an impurity in the alloy. In this study, Nb3Sn was doped with Zr to form Zr-Nb3Sn alloys. This project investigates the surface properties and chemical composition of Zr-Nb3Sn alloys with varying zirconium concentrations (~0.5% and ~24% Zr). Using Scanning Electron Microscopy (SEM), Energy Dispersive Spectroscopy (EDS), and X-ray Photoemission Spectroscopy (XPS), allowed for the characterization of the differences in surface morphology and elemental composition between samples. SEM images were quantified using ImageJ giving insight into grain distribution. The results indicate that increased Zr concentration creates smaller grains in the Zr-Nb3Sn alloy. Furthermore, the ~ 24% Zr grew nanoscale particles on the surface that are possible oxides. XPS data revealed that as Zr concentration increased, the total Nb oxides (NbOx) thickness decreased. Conversely, as Zr concentration increased, the surface Sn oxides (SnOx) also increased slightly. Quantification via ImageJ of SEM data showed that the ~ 0.5% Zr sample had a grain size of ~ 5300 nm2. These results show that Zr inclusion leads to smaller grain formations, which is promising in the world of superconducting RF cavities for high magnetic field applications.