Biopolyurethane coatings with silica-titania microspheres (MICROSCAFS®) as functional filler for corrosion protection

In this work, we studied a biopolyurethane (BioPU) coating derived from a bio-based polyol and isocyanate for the protection of carbon steel against corrosion. The direct utilization of polyols obtained from raw biomass represents a novelty in polyurethane coatings production. The protective properties of these coatings were enhanced by incorporating unique silica-titania (ST) MICROSCAFS®, which are microspheres exhibiting interconnected macro- and mesoporosity. They were loaded with tannic acid (TA), an eco-friendly corrosion inhibitor. Confirmation of TA loading into the ST carriers (therefore called ST\TA) was achieved through Attenuated total reflectance - Fourier-transform infrared spectroscopy (ATR-FTIR) and Thermogravimetric (TG) analyses. TG analysis revealed that ST\TA particles contain approximately 34 wt% TA, and their average particle diameter is approximately 25 ± 5 μm, observed by SEM. The TGA shows slightly improved thermal resistance of the coatings modified with the filler MICROSCAFS®. Furthermore, it was observed that the fillers strengthened the coating hardness without negatively affecting the adhesion strength. Electrochemical Impedance Spectroscopy (EIS) results demonstrated that all modified coatings exhibited very good to excellent resistance in mild corrosive environments. The coatings maintained a high impedance modulus (|Z|) at low frequencies and phase angle values close to −90° across a wide frequency range, over an immersion period of 80 days in a 0.05 M NaCl solution. After 80 days of immersion, the best coating, BPU-ST\TA, displayed |Z| of 3 × 10 10 Ω cm 2 . Scanning Vibrating Electrode Technique (SVET) analysis revealed the inhibitory behaviour of TA. For the BPU-ST\TA sample, inhibition of both anodic and cathodic activities was clearly visible, with a significant reduction of the current densities starting at 1 h and up to at least 24 h of immersion. In summary, the BioPU coatings modified with tannic acid-loaded MICROSCAFS® exhibit improved barrier properties and notable corrosion inhibition capacity in mild corrosive environments. • Bio-based polyurethanes, synthetized from biomass-derived polyols, were utilized as coatings for corrosion protection. • Novel Silica-Titania MICROSCAFS® with highly interconnected porosity were first used as fillers in organic coatings. • Bio-based coatings, modified with MICROSCAFS® carrying tannic acid inhibitor, show notable corrosion inhibition capacity.