Influence of process parameters on the organization and properties of 316L-SCBCC bracket formed by selective zone laser melting

Abstract 316L porous skeletal scaffolds prepared by selective laser melting (SLM) technology are currently widely used in bone injuries. Its successful implantation is predicated on having properties that match those of natural bone. The process parameters significantly influence the performance of SLM-316L porous scaffold. In this study, the nine-group shaping process parameters were determined by orthogonal method. The 316L porous scaffolds were tested in compression, electrochemistry, XRD and microstructure. The influence of process parameters on the performance of body-centered cubic peripheral square structure bracket was investigated. The influence laws of process parameters on microstructure, mechanical properties and corrosion resistance were obtained. The results show that process parameters have a significant effect on the microstructure, properties and defect distribution. The reduction of defects and grain refinement in the stent is conducive to the improvement of compressive properties and hardness of the stent. The magnitude of the hardness is inversely related to the grain size. The corrosion current density of porous scaffolds are also affected by their microscopic defects and grain size. At an energy density of 78.70 J mm −3 presents the least defects and obtains smaller grains, resulting in the best mechanical properties and corrosion resistance.