Microstructure evolution and catalytic activity of AlCo1−xFeNiTiMox high entropy alloys fabricated by powder metallurgy route

This investigation presents the synthesis of equiatomic and non-equiatomic AlCo_1-xFeNiTiMo_x (x = 0, 0.1, 0.25 and 1.0) high entropy alloys fabricated by mechanical alloying. Mo partially replaced Co. Classic thermodynamic calculations, such as mixing enthalpy (ΔH_mix), configurational entropy (ΔS_mix), the atomic size difference (δ), entropy to enthalpy ratio (Ω), electronegativity difference (△χ), and valence electron concentration (VEC) were used. Considering δ, Ω and VEC parameters, a BCC solid solution and an intermetallic phase can be predicted due to the partial replacement of Co by Mo. X-ray and electron diffraction of equiatomic HEA without Mo content revealed that after 35 h of milling, a Fe-type BCC lattice phase was formed in the alloy and two L2₁ phases, in addition to a minimal amount of FCC phase. As the Mo content increased, the Fe-type BCC phase was steadily replaced by the Mo-type BCC phase and the Fe-type FCC phase, and two L2₁ phases were also developed. When the 5 at% Mo-containing (x = 0.25) alloy was further milled for 80 h, the amount of phases remained almost the same; only the grain size was strongly reduced. The influence of the Mo addition on the properties of studied alloys was also confirmed in the decolourisation of Rhodamine B using a modified photo-Fenton process. The decolourisation efficiency within 20 min was 72% for AlCoFeNiTi and 87% for AlCo_0.75FeNiTiMo_0.25 using UV light with 365 nm wavelength.