Mn2+ doped Zn2SiO4 phosphors: A threefold-mode sensing approach for optical thermometry in the visible region at 525 nm

Optical functional materials such as nanostructured silicates have been studied for photonics applications involving energy conversion. In this scenario, we studied Zn 2 SiO 4 :Mn 2+ nanostructured powders prepared by combustion synthesis for optical thermometry based on photon downshifting. The structural analysis showed that Zn 2 SiO 4 particles were found embedded in clustered silica nanoparticles. The photoluminescence analysis showed that the samples exhibit intense green emission (centered around 525 nm), corresponding to the electronic transition 4 T 1 → 6 A 1 of Mn 2+ , when exposed to a low power ultraviolet lamp (centered around 255 nm). The temperature sensing performance of this material was evaluated using three different methodologies, i.e. the luminescence decay time constant, the spectral full width at half maximum, and the luminescence peak intensity from the 4 T 1 → 6 A 1 radiative transition. The thermometric analysis based on luminescence peak intensity provided a maximum relative sensitivity of ∼4.9x10 −3 K −1 at 498 K, while the decay lifetime and the spectral width at half maximum provided maximum relative temperature sensitivities of ∼2.9x10 −3 K −1 at 523 K and ∼1.7x10 −3 K −1 at 298 K, respectively. • Zn 2 SiO 4 :Mn 2+ ceramic powders were prepared via a combustion method. • The structural analysis showed that zinc silicate particles were found embedded in clustered silica nanoparticles. • Mn 2+ emission ( 4 T 1 .→ 6 A 1 ) changes with the temperature was studied. • Thermal sensitivities were obtained for luminescence intensity, decay time, and linewidth at half-maximum methodologies.