Establishing a process route for additive manufacturing of NiCu-based Alloy 400: an alignment of gas atomization, laser powder bed fusion, and design of experiments

Abstract Alloy 400 is a corrosion-resistant, NiCu-based material which is used in numerous industrial applications, especially in marine environments and the high-temperature chemical industry. As conventional manufacturing limits geometrical complexity, additive manufacturing (AM) of the present alloy system promises great potential. For this purpose, a robust process chain, consisting of powder production via gas atomization and a design of experiment (DoE) approach for laser powder bed fusion (LPBF), was developed. With a narrow particle size distribution, powders were found to be spherical, flowable, consistent in chemical composition, and, hence, generally applicable to the LPBF process. Copper segregations at grain boundaries were clearly detected in powders. For printed parts instead, low-intensity micro-segregations at cell walls were discovered, being correlated with the iterative thermal stress applied to solidified melt-pool-near grains during layer-by-layer manufacturing. For the production of nearly defect-free LPBF structures, DoE suggested a single optimum parameter set instead of a broad energy density range. The latter key figure was found to be misleading in terms of part densities, making it an outdated tool in modern, software-based process parameter optimization. On the microscale, printed parts showed an orientation of melt pools along the build direction with a slight crystallographic [101] texture. Micro-dendritic structures were detected on the nanoscale being intersected by a high number of dislocations. Checked against hot-extruded reference material, the LPBF variant performed better in terms of strength while lacking in ductility, being attributed to a finer grain structure and residual porosity, respectively.