Physical Properties Studies of Magnesium Phthalocyanine (MgPc) Thin Films of Different Annealing Temperatures Prepared by Pulsed Laser Deposition Technique

Magnesium Phthalocyanine (MgPc) was deposited on a glass substrate by pulsed laser deposition (PLD) using Q-Switching Nd:YAG laser with wavelength 1064 nm, repetition rate 6 Hz, at room temperature (300K) and different annealing temperatures (373, 473, and 573)K under vacuum condition of 10-3 torr. All films were annealed for one hour to attain crystallinity. X-ray diffraction (XRD) of MgPc powder indicated that MgPc crystallizes in polycrystalline with a monoclinic structure. While comparing the MgPc films, it was observed that the intensity of the characteristic peak increases with temperature, and the crystallization exhibited a monoclinic structure typical of the β-form. The Miller indices, hkl, values for each diffraction peak in the XRD spectrum were calculated. The characteristic peak of Phthalocyanine (MgPc) was found at 2θ value 6.9137ᵒ with the hkl value of (100) for both MgPc powder and deposited thin films. Field emission scanning electron microscopy (FESEM) and energy-dispersive X-ray spectroscopy (EDX) analyses indicated that crystallinity improved and surface morphology was enhanced with the rise in annealing temperature and showed uniform-sized grains. They also assisted in identifying the optimal parameters that yielded the best structural properties for the film. The optical properties of MgPc thin film showed two absorption bands. The MgPc thin films exhibit transport and onset direct energy gaps (Eg) for all samples. Additionally, the absorption coefficient (α) was calculated using Lambert Law, revealing a slight dependence on the annealing temperature.