Construction and combustion behavior of horizontal two-dimension combustion networks of boron-metal oxides

In order to break through the top-down combustion mode brought by the traditional pillars, it is explored to explore the exploration of delay composition array construction in two-dimensional dimensions. In this study, B-CuO, B-Bi 2 O 3 , B-Fe 2 O 3 sticks and combustion networks with good forming properties were prepared with the help of a micro-pen direct ink writing device by dispersing the above materials in DMF with boron and metal oxides as the main body of the charge and F 2602 as the binder. The sticks were thermally ignited using a nichrome wire, and the flame propagation behaviors of the sticks with different formulations, spacings and heights were tracked with a high-speed camera, and a series of combustion networks were designed on the premise of not leaping into flames. Results show that the B-CuO stick has the fastest ignition speed level (19.71–29.02 mm ·s −1 ) at equivalence ratios of 1.0–4.0, followed by B-Bi 2 O 3 (5.99–16.01 mm ·s −1 ) and B-Fe 2 O 3 is the slowest (1.91–4.94 mm ·s −1 ). The sticks burned best at an equivalence ratio of 1.0–1.5. A variety of combustion networks were constructed on 50 × 50 mm glass slides by selecting B-CuO, B-Bi 2 O 3 , and B-Fe 2 O 3 at the equivalence ratios of 1.0, 1.5, and 1.5, respectively, among which B-CuO had the shortest combustion time (5.17 s), the shortest total combustion network length (252 mm), and 400 mm network could be realized for B-Bi 2 O 3 . Construction and 19.85 s, and B-Fe 2 O 3 can realize 608 mm network length and 130.7 s combustion time. Through these studies, the two-dimensional combustion network construction of boron-metal oxides was realized, which provides a new idea for the delay action in small size. With the help of micro-pen direct writing process, we have subverted the top-down combustion mode of traditional medicine column funding. A single-input single-output combustion network is constructed in the plane using boron and metal oxides, which has good combustion effect and can realize stable combustion of 2–160s in 50 × 50 × 2 mm. • The DIW (Direct ink writing) process of B-CuO, B-Bi 2 O 3 , and B-Fe 2 O 3 was successfully explored and tested for their combustion properties. • It breaks through the top-down combustion mode of traditional pillars and realizes the customized combustion of energetic materials in a two-dimensional plane. • The effects of different stick angles on combustion stability were explored, providing feasible ideas for the design of combustion networks.