Study on the Relationship between Electron Transfer and Electrical Properties of XLPE/Modification SR under Polarity Reversal

The insulation of high-voltage direct-current (HVDC) cables experiences a short period of voltage polarity reversal when the power flow is adjusted, leading to sever field distortion in this situation. Consequently, improving the insulation performance of the composite insulation structure in these cables has become an urgent challenge. In this paper, SiC-SR (silicone rubber) and TiO₂-SR nanocomposites were chosen for fabricating HVDC cable accessories. These nanocomposites were prepared using the solution blending method, and an electro-acoustic pulse (PEA) space charge test platform was established to explore the electron transfer mechanism. The space charge characteristics and field strength distribution of a double-layer dielectric composed of cross-linked polyethylene (XLPE) and nano-composite SR at different concentrations were studied during voltage polarity reversal. Additionally, a self-built breakdown platform for flake samples was established to explore the effect of the nanoparticle doping concentration on the breakdown field strength of double-layer composite media under polarity reversal. Therefore, a correlation was established between the micro electron transfer process and the macro electrical properties of polymers (XLPE/SR). The results show that optimal concentrations of nano-SiC and TiO₂ particles introduce deep traps in the SR matrix, significantly inhibiting charge accumulation and electric field distortion at the interface, thereby effectively improving the dielectric strength of the double-layer polymers (XLPE/SR).