Mechanical and Drying Shrinkage Performance Study of Ultra-High-Performance Concrete Prepared from Titanium Slag under Different Curing Conditions

This research investigates the effects of various curing regimes, the incorporation of titanium slag, and the utilization of quartz sand on the strength properties and shrinkage behavior of ultra-high-performance concrete (UHPC). By using low-heat silicate cement to prepare UHPC, this study conducted standard curing and steam curing, and comprehensively analyzed the macro and micro performance of UHPC under different curing conditions. The findings indicate that the application of steam curing markedly enhances the mechanical attributes of UHPC while efficiently decreasing its drying shrinkage. In the comparative tests, we found that the compressive strength of concrete that had undergone 2 days of steam curing was 9.15% higher than that of concrete cured for 28 days under standard conditions. In addition, under the same curing conditions, titanium slag sand had higher mechanical properties than quartz sand. Under standard curing conditions, the 28-day compressive strength of UHPC using titaniferous slag aggregate was 12.64% higher than that of UHPC using standard sand. Through the data analysis of XRD, TG, and MIP, we found that the content of Ca(OH)₂ in the hydration products after steam curing was reduced compared to the standard curing conditions, and the pore structure had been optimized. The UHPC prepared with titanium slag sand has greater advantages in mechanical properties and drying shrinkage, and has a smaller pore structure than the UHPC prepared with quartz sand. Moreover, the use of titanium slag sand offers ecological and economic benefits, making it a more sustainable and cost-effective option for high-performance construction applications.