Modified Hybrid Hydroxyapatite-Silver Nanoparticles Activated via a Blue Light Source in Various Concentrations in Two-Step Self-Etch Adhesive to Caries-Affected Primary Dentin

<b><i>Aims:</i></b> To evaluate hydroxyapatite-silver (HA-Ag) hybrid nanoparticles (NPs), as an antibacterial agent when integrated in self-etch (SE) adhesive. Blue light activated HA-Ag hybrid NP incorporation on mechanical properties, degree of conversion (DC), and microtensile bond strength (μTBS). <b><i>Method:</i></b> Eighty primary molar teeth have carious lesions reaching the dentin but not involving the pulp. The infected dentin was removed and carious-affected dentin (CAD) was preserved. Forty samples were inoculated with <i>Streptococcus mutans</i>. All primary teeth (<i>n</i> = 80) were allocated into four groups based on the incorporation of HA-Ag hybrid NPs in different concentrations (0%, 1%, 5%, and 10%). Group 1: 0% HA-Ag hybrid NPs + Clearfil SE bond primer, group 2: 1% HA-Ag hybrid NPs + Clearfil SE bond primer, group 3: 5 wt% HA-Ag NPs + Clearfil SE bond primer, and group 4: 10 wt% HA-Ag NPs + Clearfil SE bond primer. The survival rate assessment of <i>S. mutans</i> was conducted on 40 inoculated samples. On the remaining primary teeth (<i>n</i> = 40), Clearfil SE bonding agent was applied uniformly via a blue light source. The composite buildup was performed on the samples and μTBS and failure analysis assessed. Fourier transform infrared spectroscopy was performed to assess DC. Survival rates of <i>S. mutans</i> and μTBS among the tested groups were compared using ANOVA and Tukey post hoc analysis. <b><i>Results:</i></b> 10 wt % HA-Ag NPs + Clearfil SE bond primer exhibited the highest level of antibacterial efficacy (0.14 ± 0.02 CFU/mL) against <i>S. mutans</i>. The highest μTBS (18.38 ± 0.78 MPa) at the composite/CAD interface was in group 2 (1 wt % HA-Ag NPs + Clearfil SE bond primer + Clearfil SE bonding agent + activation with a blue light source). The highest DC was observed in the control group with Clearfil SE bond primer + Clearfil SE bonding agent + activation with a blue light source. <b><i>Conclusion:</i></b> 1 wt% HA-Ag hybrid NPs showed enhanced antibacterial effectiveness, DC, and bond strength of the SE adhesive to the primary CAD.