MIL-Derived Hollow Tubulous-Shaped In2O3/ZnIn2S4 Z-Scheme Heterojunction for Efficient Antibacterial Performance via In Situ Composite

In this study, a hollow tubulous-shaped In₂O₃ derived from MIL (MIL-68 (In)) exhibited an enhanced specific surface area compared to MIL. To further sensitize In₂O₃, ZnIn₂S₄ was grown in situ on the derived In₂O₃. The 40In₂O₃/ZnIn₂S₄ composite (1 mmol ZnIn₂S₄ loaded on 40 mg In₂O₃) exhibited degradation rates of methyl orange (MO) under visible light (80 mW·cm^-2, 150 min) that were 17.9 and 1.4 times higher than those of the pure In₂O₃ and ZnIn₂S₄, respectively. Moreover, the 40In₂O₃/ZnIn₂S₄ exhibited an obviously improved antibacterial performance against <i>Pseudomonas aeruginosa</i>, with an antibacterial rate of 99.8% after visible light irradiation of 80 mW cm^-2 for 420 min. The 40In₂O₃/ZnIn₂S₄ composite showed the highest photocurrent density, indicating an enhanced separation of photogenerated charge carriers. Electron spin resonance results indicated that the 40In₂O₃/ZnIn₂S₄ composite generated both ·O₂^- and ·OH radicals under visible light, whereas ·OH radicals were almost not detected in ZnIn₂S₄ alone, suggesting the presence of a Z-scheme heterojunction between In₂O₃ and ZnIn₂S₄, thereby enhancing the degradation and antibacterial capabilities of the composite. This offers fresh perspectives on designing effective photocatalytic materials for use in antibacterial and antifouling applications.