Reactive Condensation of Cr Vapor on Aluminosilicates Containing Alkaline Oxides

This study is part of a series with the objective of improving fundamental understanding of reactive condensation of Chromium (Cr) vapors, which are generated from Cr containing alloys used in many high-temperature (>500 °C) process environments and can form potentially problematic condensed hexavalent (Cr(VI)) species downstream. This study specifically focuses on the effects of alkaline oxide additives in aluminosilicate fibers on Cr condensation and speciation. Cr vapors were generated by flowing high-temperature (800 °C) air containing 3% water vapor over chromia (Cr 2 O 3 ) powder, with aluminosilicate fiber samples positioned downstream where the temperature decreases (<500 °C). Total condensed Cr and ratios of oxidation states were measured using inductively coupled plasma optical emission spectroscopy (ICP-OES) and diphenyl carbazide (DPC) colorimetric/direct UV–vis spectrophotometric analyses. Results indicate presence of hexavalent Cr (Cr(VI)) species condensed on all samples investigated. The ratio of Cr(VI) to total Cr detected was consistently higher on aluminosilicate fiber samples containing alkaline oxide (CaO and MgO) additions. Computational thermodynamic equilibrium modelling corroborated experimental results showing stabilities of Ca and Mg chromate (Cr(VI)) compounds. Comparative results and analyses are presented and discussed to help inform mechanistic understanding and future related research and engineering efforts.