Depth-resolved deuterium retention analysis in displacement-damaged tungsten using laser-induced breakdown spectroscopy

Fuel retention in plasma-facing components (PFCs) is a critical issue in future nuclear fusion reactors operating with Deuterium-Tritium (DT) regarding nuclear safety and fulfillment of the T cycle. However, during DT plasma operation, highly energetic neutrons will induce damage in the lattice of W PFCs causing enhanced fuel retention in defects or traps. Laser-Induced Breakdown Spectroscopy (LIBS) is a potential tool to monitor the T-content in situ in PFCs of future nuclear fusion devices. This article presents an ex situ study on pre-damaged W material after D plasma exposure to qualify the method and mimic conditions expected in a reactor. ITER grade W samples were displacement-damaged by 10.8 MeV W ions to a damage dose of 0.23 dpa and exposed to low temperature deuterium plasma at low energy in PlaQ. The resulting deuterium concentration was analyzed by using 3He Nuclear Reaction Analysis (depth resolution of ≈150 nm) as a well-established method, and LIBS (picosecond laser pulses, depth resolution of 15 nm). The sample with the highest deuterium concentration showed a deuterium-rich zone up to a depth of 1.13 μm using both techniques. This is close to the expected W ion-induced damage depth of ≈1 μm. The results imply that LIBS as an in situ technique for tritium monitoring could be a viable option for a reactor.