THE PREPARATION AND CHARACTERIZATION OF A LANTHANUM-BASED RARE EARTH CONVERSION COATING ON MAGNESIUM ALLOY AZ91D AND ITS DEGRADATION IN 3.5% NaCl SOLUTION

Magnesium alloys have a huge market and broad prospects due to their high specific strength, good ductility, and strong thermal conductivity. However, the active chemical properties of elemental magnesium and the negative standard electrode potential result in magnesium alloys being highly susceptible to corrosion and failure. Chemical conversion treatment of magnesium alloy can improve its corrosion resistance by preparing a chemical conversion film on its surface. Rare earth conversion treatment has the advantages of effortless process, moderate price, no pollution, good corrosion resistance, and synergistic effect with inorganic or organic additives, which is in line with the pursuit of “green chemical” in industrial production. At present, there is little research and application on lanthanum-based rare earth conversion coatings (La-RECC). This paper selects rare earth element lanthanum (La) to prepare La-RECC on the surface of AZ91D magnesium alloy through chemical conversion treatment. The microstructure, chemical composition, and protective properties of La-RECC were discovered, as well as their interrelationships, revealing the degradation process of La-RECC in 3.5% NaCl solution. La-RECC is composed of La(OH) 3 and Mg(OH) 2 , exhibiting a crystal cluster structure with cracks, and there are a large number of needle-like crystals on the crystal cluster of La-RECC, with a thickness of 2.14 [Formula: see text]m. The degradation process of La-RECC can be divided into three stages: Rapid degradation, slow degradation, and complete degradation. The complete degradation time of La-RECC in 3.5% NaCl solution is 82.5[Formula: see text]h.