Effect of Si Addition in NiCrAl Coating on Corrosion in Molten Nitrate Salt

The materials used in concentrating solar power (CSP) systems are becoming of interest because of the high energy efficiency of energy storage. Molten salts can be used as both heat-storage media and heat-transfer fluid in a CSP system. In molten salts, steel alloys used in vessels and pipelines are highly vulnerable to hot corrosion. To protect steel alloys, applying a coating is an excellent strategy to extend the life of the alloy. NiCrAl coatings are well-suited for high-temperature environments. The purpose of this study was to investigate the corrosion behavior of NiCrAl with Si addition coatings on AISI304 in molten salt. NiCrAl coatings with and without Si addition were deposited using the high-velocity oxygen fuel (HVOF) technique. The corrosion test was performed using an immersion test in modified solar salt with 0.5% NaCl at 400–600 °C. Gravimetric methods evaluate the weight change for immersion tests. At 400 °C, an increased amount of weight gain due to the oxidation reaction and molten salt infiltration was observed. At 600 °C, the corrosion reaction was more dominant, and apparent oxidation was decreased; however, oxidation products NiO and sodium aluminum silicate were detected. Si addition supports the formation of the protective oxide sodium aluminum silicate, which inhibits molten salt oxidation reaction and molten salt infiltration.