An order-disorder core-shell strategy for enhanced work-hardening capability and ductility in nanostructured alloys
Nanocrystalline metallic materials have the merit of high strength but usually suffer from poor ductility and rapid grain coarsening, limiting their practical application. Here, we introduce a core-shell nanostructure in a multicomponent alloy to address these challenges simultaneously, achieving a high tensile strength of 2.65 GPa, a large uniform elongation of 17%, and a high thermal stability of 1173 K. Our strategy relies on an ordered superlattice structure that excels in dislocation accumulation, encased by a ≈3 nm disordered face-centered-cubic nanolayer acting as dislocation sources. The ordered superlattice with high anti-phase boundary energy retards dislocation motions, promoting their interaction and storage within the nanograins. The disordered interfacial nanolayer promotes dislocation emission and effectively accommodates the plastic strain at grain boundaries, preventing intergranular cracking. Consequently, the order-disorder core-shell nanostructure exhibits enhanced work-hardening capability and large ductility. Moreover, such core-shell nanostructure exhibits high coarsening resistance at elevated temperatures, enabling it high thermal stability. Such a design strategy holds promise for developing high-performance materials.
Authors
- Junhua Luan (ORCID: https://orcid.org/0000-0002-0736-200X)
- Zhihao Jiang (ORCID: https://orcid.org/0000-0002-2688-6255)
- W.H. Zhou (ORCID: https://orcid.org/0000-0001-9296-818X)
- Xin Zhou (ORCID: https://orcid.org/0000-0002-1820-7830)
- Fenghui Duan (ORCID: https://orcid.org/0000-0002-7601-2572)
- Jie Pan (ORCID: https://orcid.org/0000-0001-5465-0736)
- Qian Li (ORCID: https://orcid.org/0000-0003-1452-7121)
- Tao Yang (ORCID: https://orcid.org/0000-0003-4355-9210)
- Jian Lü (ORCID: https://orcid.org/0000-0001-5362-0316)
- Shiyuan Zhang (ORCID: https://orcid.org/0000-0002-1123-9821)
- Lin Zhou (ORCID: https://orcid.org/0000-0001-9340-6840)
- Zheling Shen
Institutions
- University of Science and Technology of China (CN)
- City University of Hong Kong (HK)
- Chinese Academy of Sciences (CN)
- City University of Hong Kong, Shenzhen Research Institute (CN)
- Huazhong University of Science and Technology (CN)
Publication Details
- Journal
- Nature Communications
- Published
- 2024-08-09
- DOI
- https://doi.org/10.1038/s41467-024-50984-9
- Citations
- 24
- Primary Topic
- High Entropy Alloys Studies
- Type
- article
- Field-Weighted Citation Impact
- 5.10
Funders
- City University of Hong Kong
- National Natural Science Foundation of China
- Research Grants Council, University Grants Committee
- Innovation and Technology Commission