Analysis of the Surface Morphology and Chemical Composition of Zr-Nb3Sn Alloys with Zr Different Concentrations

The inclusion of zirconium (Zr) in niobium-tin (Nb3Sn) significantly enhances the performance of Nb3Sn radiofrequency cavities in high magnetic fields. This research project is dedicated to characterizing the surface properties and chemical composition of Zr-doped Nb3Sn. Two different concentrations of Zr were used for doping: approximately 0.5% and 24%. Various spectroscopy techniques were employed to analyze how the surface morphology and chemical composition of Nb3Sn change with increasing Zr content. The findings of this study indicate that the grain size decreases as the Zr concentration increases. In samples with 24% Zr, nanometer-sized particles, likely oxides, were observed. X-ray photoelectron spectroscopy (XPS) data revealed that the thickness of niobium oxides (NbOx) decreases with increasing Zr, while the thickness of tin oxides (SnOx) increases. Additionally, grain size distribution analysis showed that the average grain size is around 5300 nm , with a grain area density of about 165 grains/μm .