An Initial Evaluation of the Elevated-Temperature Cyclic Properties of Optimized 316H Stainless Steel Fabricated by Powder Metallurgy Hot Isostatic Pressing

The process of powder metallurgy (PM) hot isostatic pressing (HIP) works by consolidating powdered materials at relatively high temperature and pressure to form near-net-shaped components. Ideally, PM-HIP production methods can reduce component lead time and improve designs for high-temperature reactors and/or microreactors. To introduce PM-HIP into Section III, Division 5 of the American Society of Mechanical Engineers Boiler and Pressure Vessel Code, it is necessary to show adequate material properties regarding creep, high-temperature low-cycle fatigue, and creep fatigue. However, prior work has shown that the creep-fatigue cycles to failure for PM-HIP 316H stainless steel are greatly reduced compared to the conventional, wrought product. This work continued creep-fatigue analysis on a 316H stainless steel with lower oxygen and nitrogen contents and at different HIP parameters than previously analyzed. The objective was to better understand what is causing the reduced PM-HIP 316H performance so improvements can be made PM-HIP 316H creep-fatigue lifetimes.